Caracterización mecánica de la tenacidad a la fractura en modo II de materiales estructurales ligeros de ingeniería
Para citar o enlazar este item, por favor use el siguiente identificador:
http://dspace.ups.edu.ec/handle/123456789/28320| Title: | Caracterización mecánica de la tenacidad a la fractura en modo II de materiales estructurales ligeros de ingeniería |
| Authors: | Berrezueta Arias, Mateo Nicolás |
| Advisor: | Santos Benítez, Jonnathan Darío |
| Abstract: | This study experimentally investigates the mechanical properties and mode II interlaminar fracture toughness of a continuous glass fiber-reinforced composite, fabricated using the Markforged MarkTwo® 3D printer. Due to the lack of information on this material, glass fiber specimens were printed and tested. The failure analysis of the specimens was conducted using a scanning electron microscope (SEM), allowing observation of the microstructure and defects at the microscopic level. |
| Translated abstract: | Este estudio investiga experimentalmente las propiedades mecánicas y la tenacidad a la fractura interlaminar en modo II de un compuesto reforzado con fibra continua de vidrio, fabricado con la impresora 3D Markforged MarkTwo®. Debido a la falta de información sobre este material, se imprimieron y ensayaron probetas de fibra de vidrio. El análisis del fallo de las probetas se realizó con un microscopio electrónico de barrido (SEM), permitiendo observar la microestructura y los defectos a nivel microscópico. |
| Keywords: | INGENIERÍA CIVIL FIBRA DE VIDRIO PROPIEDADES DE LA MATERIA MECÁNICA DE FRACTURA IMPRESIÓN TRIDIMENSIONAL MATERIALES |
| Issue Date: | Jul-2024 |
| URI: | http://dspace.ups.edu.ec/handle/123456789/28320 |
| Language: | spa |
| Appears in Collections: | Grado |